Didymium glasses

Didymium (Greek: δίδυμο, twin element) is a mixture of the elements praseodymium and neodymium. It is used in safety glasses for glassblowing and blacksmithing, especially with a gas (propane)-powered forge, where it provides a filter that selectively blocks the yellowish light at 589 nm emitted by the hot sodium in the glass, without having a detrimental effect on general vision, unlike dark welder's glasses. The strong infrared light emitted by the superheated forge gases and insulation lining the forge walls is also blocked thereby saving the crafters' eyes from serious cumulative damage such as glassblower's cataract. The usefulness of didymium glass for eye protection of this sort was discovered by Sir William Crookes.

Didymium photographic filters are often used to enhance autumn scenery by making leaves appear more vibrant. It does this by removing part of the orange region of the color spectrum, acting as an optical band-stop filter. Unfiltered, this group of colors tends to make certain elements of a picture appear "muddy". These photographic filters are also used by nightscape photographers as they absorb part of the light pollution caused by sodium street lights. Didymium was also used in the sodium vapor process for matte work due to its ability to absorb the yellow color produced by its eponymous sodium lighting.

Didymium is also used in calibration materials for spectroscopy.[1]


Didymium ('Di=95') in the first edition periodic table of Mendeleev

Didymium was discovered by Carl Mosander in 1841.[2] It was named after the Greek work δίδυμο (twin) because it is very similar to lanthanum and cerium, with which it was found.[3] Mosander wrongly believed didymium to be an element,[4] under the impression that "ceria" (sometimes called cerite) isolated by Jöns Jakob Berzelius in 1803 was really a mixture of cerium, lanthanum, and didymium.[citation needed] He was right about lanthanum's being an element, but not about didymium. Since spectroscopy had not yet been invented, Mosander did as well as could be expected at the time. His three "elements" accounted for at least 95% of the rare earths in the original cerite from Bastnäs, Sweden.

Didymium had not been difficult to find, since in trivalent form it tinged the salts of ceria pink. During the period when didymium was believed to be an element, the symbol Di was used for it. In the illustration of Mendeleev's first attempt at a periodic table, shown on the right, the atomic weights assigned to the various lanthanides, including didymium, reflect the original belief that they were divalent. Their actual oxidation number of 3 implies that Mendeleev underestimated atomic weights for them by 13.

In 1874, Per Teodor Cleve deduced that didymium was made up of at least two elements.[3] In 1879, Lecoq de Boisbaudran succeeded in isolating samarium, from didymium contained in North Carolinian samarskite. Then in 1885, Carl Auer von Welsbach succeeded in separating salts of the last two component elements,[4][5] praseodymium and neodymium.[2] The method used was a fractional crystallization of the double ammonium nitrates from a solution of nitric acid.[4]

Welsbach had decided to name his two new elements "praseodidymium" ("green didymium") and "neodidymium" ("new didymium"), but one syllable was soon dropped from each name. Despite being abbreviated in the new elements' names, the untruncated name "didymium" persisted, partly due to its use as an ingredient in glassblowers' goggles, and colored glass.[4] The name "didymium" also was retained in mineralogical texts.[3]


During World War I, didymium mirrors were reportedly used to transmit Morse Code across battlefields.[3] Didymium does not absorb enough light to make the variation in lamp's light output obvious, but someone with binoculars attached to a prism in the correct fashion could see the absorption bands flash on and off.

In the late 1920s, Leo Moser (Moser glass-works Director General, 1916 to 1932) recombined praseodymium and neodymium in a 1:1 ratio to create his "Heliolite" glass ("Heliolit" in Czech), which has color-changing properties between amber, reddish, and green depending on the light source. This was one of a number of decorative glasses using rare earth colorants, with "Heliolit" and "Alexandrit" being the first two, introduced by Moser in 1929. Leo Moser's papers in the Corning Glass Museum make it clear that the first experimental glass melts done by Moser involving any of the rare earths occurred in November 1927.

After a year of further development, the rare earth glasses were introduced to great acclaim at the Spring 1929 trade show in Leipzig. The Alexandrit and Heliolit names were registered as trademarks in June 1929. The earlier date of 1925 sometimes given for rare earth glass refers to an award for glass design, not glass composition.[6]

Industrial use

The name "didymium" continued to be used in the rare earth metal industry. In the US, commercial "didymium" salts were what remained after cerium had been removed from the natural products obtained from monazite, and thus it contained lanthanum, as well as Mosander's "didymium". A typical composition might have been 46% lanthanum, 34% neodymium, and 11% praseodymium, with the remainder mostly being samarium and gadolinium, for material extracted from South African "rock monazite" from the Steenkampskraal mine.[3]

Typically, in ores, neodymium is higher in relative abundance in monazite, as compared to the bastnäsite compositions, and the difference is noticeable when unseparated mixtures derived from each are examined side-by-side: the monazite-derived products are more pinkish, and the bastnäsite-derived products are more brownish in tinge, due to the latter's increased relative praseodymium content. (The original cerite from Bastnäs has a rare earth composition highly similar to that of monazite sand.)[citation needed]

The European use was closer to Mosander's concept. Such cerium-depleted light lanthanide mixtures have been widely used to make petroleum-cracking catalysts. The actual ratio of praseodymium to neodymium varies somewhat depending on the source of the mineral, but it is often around 1:3. Neodymium always dominates, which is why it got the "neo" appellation, being responsible for most of the color of the old didymium in its salts.[citation needed]


  1. ^ Venable, W.H.; Eckerle, K.L. (October 1979). Didymium glass filters for calibrating the wavelength scale of spectrophotometers: SRMs 2009, 2010, 2013, and 2014. National Institute of Standards and Technology. NIST (Report). U.S. Department of Commerce. NIST doc 10486.
  2. ^ a b Emsley, John (2003). Nature's building blocks: an A–Z guide to the elements. Oxford University Press. p. 341. ISBN 0-19-850340-7.
  3. ^ a b c d e Fontani, Marco; Costa, Mariagrazia; Orna, Mary Virginia (2015). The Lost Elements: The Periodic Table's Shadow Side. Oxford University Press. pp. 172–173. ISBN 978-0-19-938334-4.
  4. ^ a b c d Haynes, William M., ed. (2016). "Elements: Neodymium". CRC Handbook of Chemistry and Physics (97th ed.). CRC Press. p. 4.23. ISBN 9781498754293.
  5. ^ von Welsbach, Carl Auer (1885). "Die Zerlegung des Didyms in seine Elemente". Monatshefte für Chemie. 6 (1): 477–491. doi:10.1007/BF01554643.
  6. ^ Langhamer, Antonín (2003). The Legend of Bohemian Glass: A thousand years of glassmaking in the heart of Europe. Tigris. p. 134. ISBN 978-80-86062-11-2.

This page was last updated at 2021-05-11 13:05 UTC. Update now. View original page.

All our content comes from Wikipedia and under the Creative Commons Attribution-ShareAlike License.


If mathematical, chemical, physical and other formulas are not displayed correctly on this page, please useFirefox or Safari